3D Bioplotter Research Papers

Porous scaffolds were 3D-printed using poly lactic-co-glycolic acid (PLGA)/TiO2 composite (10:1 weight ratio) for bone tissue engineering applications. Addition of TiO2 nanoparticles improved the compressive modulus of scaffolds. Differential scanning calorimetry (DSC) and thermogravimetric analysis (TGA) revealed an increase in both glass transition temperature and thermal decomposition onset of the composite compared to pure PLGA. Furthermore, addition of TiO2 was found to enhance the wettability of the surface evidenced by reducing the contact angle from 90.5 ± 3.2 to 79.8 ± 2.4 which is in favor of cellular attachment and activity. The obtained results revealed that PLGA/TiO2 scaffolds significantly improved osteoblast proliferation compared to…

The bioactivity of sol–gel synthesized poly(ε-caprolactone) (PCL)/TiO2 or poly(ε-caprolactone)/ZrO2 particles was already known. In designing innovative 2D composite substrates for hard-tissue engineering, the possibility to embed PCL/TiO2 or PCL/ZrO2 hybrid fillers into a PCL matrix was previously proposed. In the present study, the potential of 3D fiber-deposition technique to design morphologically controlled scaffolds consisting of PCL reinforced with PCL/TiO2 or PCL/ZrO2 hybrid fillers was demonstrated. Finite element analysis was initially carried out on 2D substrates to find a correlation between the previously obtained results from the small punch test and the Young’s modulus of the materials, whilst mechanical and biological…